PC/PBT DPCF2200 LANXESS GERMANY

Form：Granules | Grade：Flame retardant grade

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30℃-30°C	ISO 179/1eU	170	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23℃23°C	ISO 179/1eU	No Break
Impact strength of cantilever beam gap	-30℃-30°C	ISO 180-1A	< 10	kJ/m²
	Impact strength of cantilever beam gap	0℃0°C	ISO 180-1A	11	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃23°C	ISO 180-1A	10	kJ/m²
Suspended wall beam without notch impact strength	-30℃-30°C	ISO 180/1U	150	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23℃23°C	ISO 180/1U	No Break
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23℃23℃	ISO 527-1-2	2400	Mpa
tensile strength	Yield，23℃Yield，23℃	ISO 527-2/50	45	Mpa
Tensile strain	Yield，23℃Yield，23℃	ISO 527-2/50	2.9	%
Nominal tensile fracture strain	23℃23℃	ISO 527-2/50	> 15	%
Bending modulus	23℃23℃4	ISO 178-A	2500	Mpa
bending strength	3.50% Strain3.5% Strain	ISO 178-A	70	Mpa
bending strength	bending strength	23℃23°C	ISO 178	75	Mpa
Bending strain			5	%
Ball Pressure Test		ISO 2039-1	104	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa，Unannealed1.8 MPa，Unannealed	ISO 75-2/A	75	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa，Unannealed0.45 MPa，Unannealed	ISO 75-2/B	95	°C
Vicat softening temperature	B120B120	ISO 306/B120	118	°C
Ball indentation test	115℃115℃	IEC 60695-10-2	Pass
Melting temperature		ISO 11357-3	225	°C
Linear coefficient of thermal expansion	TD：23~55℃TD：23 to 55℃	ISO 11359-2	0.00010	1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23~55℃MD：23 to 55℃	ISO 11359-2	0.000080	1/℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.31	g/cm³
Apparent density		ISO 60	0.8	g/cm³
Melt Volume Flow Rate (MVR)	260℃，5 kg260℃/5.0 kg	ISO 1133	15	cm3/10min
Shrinkage rate	TD：250℃，2.0 mmAcross Flow : 482°F, 0.0787 in 22	ISO 294-4	0.9	%
	Shrinkage rate	TD：120℃，2.0 mm，2 hrsAcross Flow : 120°C, 2 hr, 2.00 mm 33	ISO 294-4	0.5	%
		Shrinkage rate	MD：250℃，2.0 mmFlow : 482°F, 0.0787 in 22	ISO 294-4	0.9	%
		Shrinkage rate	Shrinkage rate	MD：120℃，2.0 mm，2 hrsFlow : 120°C, 2 hr, 2.00 mm 33	ISO 294-4	0.5	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Relative permittivity	23℃，100 Hz23°C, 100 Hz	IEC 60250	3.3
Relative permittivity	Relative permittivity	23℃，1 MHz23°C, 1 MHz	IEC 60250	2.9
Dissipation factor	23℃，100 Hz23°C, 100 Hz	IEC 60250	0.025
Dissipation factor	Dissipation factor	23℃，1 MHz23°C, 1 MHz	IEC 60250	0.014
flame retardant performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75 mm	UL 94	V-0
Glow wire combustion index (GWFI)	0.80 mm0.8 mm	IEC 60695-2-12	960	°C
Ignition temperature of heating wire	0.8 mm0.8 mm	IEC 60695-2-13	800	°C
	Ignition temperature of heating wire	1.6 mm1.6 mm	IEC 60695-2-13	800	°C
	Ignition temperature of heating wire	Ignition temperature of heating wire	3 mm3.0 mm	IEC 60695-2-13	800	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.