PCTG 6002 EASTMAN USA

Form：Granules | Grade：Injection grade

Properties:

Chemical resistanceHydrolysis resistance

Typical Applications:

Electrical applicationsHousehold daily necessities

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical applications \| Household daily necessities
Properties:	Chemical resistance \| Hydrolysis resistance

Certificates

No Data...

Technical Data Sheet

machinability	Test Condition	Test Method	Test Result	Test Unit
film temperature			15-30℃(60-80℉)
drying temperature			70℃(160℉)
Processing melting temperature			230-280℃(450-530℉)
drying time			6小时
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.2 mm	UL 94	V-2
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
density		D792	1.2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ASTM D638	60.0	Mpa
elongation	Break	ASTM D638	15	%
Stretching degree	@Yield	D638	5%
Stretching degree	Stretching degree	@Break	D638	320%
Bending modulus		D790	2000MPa(2.9×10
Bending modulus	Bending modulus		ISO 178	1850MPa
bending strength		ISO 178	65MPa
Tensile modulus		ISO 527	1800MPa
Impact resistance (perforation), energy @ maximum load	@23℃(73℉)	D3763	42 J(31 ft bf)
Impact resistance (perforation), energy @ maximum load	Impact resistance (perforation), energy @ maximum load	@-40℃(-40℉)	D3763	48 J/m(35 ft bf)
Impact strength of cantilever beam gap	@23℃，切口	ISO 180	7.8kJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	@-40℃，切口	ISO 180	4.8kJ/m
Tensile stress	@Yield	D638	47MPa（6900 psi）
Tensile stress	Tensile stress	@Break	D638	51MPa（7400 psi）
tensile strength	@Yield	ISO 527	47MPa
tensile strength	tensile strength	@Break	ISO 527	46MPa
Rockwell hardness	R刻度	D785	103
Impact strength of cantilever beam gap	@23℃(73℉)，未切口	D4812	NB J/m(NB ft bf/in)
	Impact strength of cantilever beam gap	@-40℃(-40℉)，未切口	D4812	NB J/m(NB ft bf/in)
		Impact strength of cantilever beam gap	@23℃(73?H)，切口	D256	80 J/m(1.5 ft bf/in)
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	@-40℃(-40?H)，切口	D256	40 J/m(0.7 ft bf/in)
Stretching degree	@Yield	ISO 527	4%
Stretching degree	Stretching degree	@Break	ISO 527	200%
tensile strength	Yield	D790	69MPa(10000 psi)
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			120	°C
drying time			3.0 to 4.0	hr
Temperature at the rear of the barrel			265 to 275	°C
Temperature in the middle of the barrel			280 to 290	°C
Spray nozzle temperature			285 to 295	°C
Processing (melt) temperature			280 to 290	°C
Mold temperature			60 to 80	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ASTM D648	135	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	125	°C
Bending temperature	0.455MPa(66 psi)	D648	73℃(164℉)
Bending temperature	Bending temperature	1.82MPa(264 psi)	D648	65℃(149℉)
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	20	g/10 min
Water absorption rate	Saturation, 23°C	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
Transmittance rate		D1003	89%
Total transmittance		D1003	91%
gloss		D1003	0.3%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	> 1.0E+16	ohms·cm
Dielectric strength	2.00 mm	ASTM D149	15	KV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.