Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 1.4 % |
| Shrinkage rate | | 内部方法 | 1.3 % |
| density | | ASTM D1505 | 0.910 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 35 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 80 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D2457 | 80 |
| Haze ratio | | ASTM D1003 | 12 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Melt Temperature | | ASTM D2117 | 150 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTM D638 | 29.4 MPa |
| tensile strength | Break | ASTM D638 | 17.7 MPa |
| elongation | Break | ASTM D638 | 600 % |
| Flexural modulus | | ASTM D790 | 1230 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 34 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 54 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | -20.0 °C |
| vicat | | ASTM D1525 | 130 °C |
| Heat distortion temperature | | ASTM D648 | 90.0 °C |
| Heat distortion temperature | | ASTM D648 | 50.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.