Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 0.60 -- |
| Shrinkage rate | | % | 0.10 -- |
| Water absorption rate | | % | 7.0 -- |
| Water absorption rate | | % | 2.0 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | MPa | 210 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | HB -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 70 |
| Impact strength of simply supported beam without notch | | kJ/m² | 85 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 9500 6000 |
| Tensile stress | | MPa | 185 |
| Tensile strain | | % | 4.0 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | -- 1E+12 |
| Volume resistivity | | ohms·cm | 1E+14 1E+13 |
| dielectric strength | | kV/mm | 40 37 |
| CTI | | V | -- 500 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 205 -- |
| | °C | 135 -- |
| Continuous use temperature | | °C | 100到120 -- |
| Continuous use temperature | | °C | 200 -- |
| Melting temperature 4 | | °C | 222 -- |
| | cm/cm/°C | 2E-05 -- |
| | cm/cm/°C | 1.1E-04 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices