Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | Resin | | 100 |
| Thermosetting components | Hardener | | 按重量计算的混合比:15 |
| Thermosetting components | | | 30 min |
| Thermosetting mixed viscosity | | ASTM D2393 | 1970 cP |
| stripping time | | | 720 min |
| stripping time | | | 60 min |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.17 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 81 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 54.7 MPa |
| bending strength | | ASTM D790 | 95.6 MPa |
| compressive strength | | ASTM D695 | 106 MPa |
| shear strength | | ASTM D732 | 5.39 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 8.4E+14 ohms·cm |
| dielectric strength | | ASTM D149 | 84 kV/mm |
| dielectric constant | | ASTM D150 | 4.06 |
| Dissipation Factor | | ASTM D150 | 1E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTME831 | 9.4E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.