PLA F 1130
0
- Usages:film
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.40 g/cm³ | |
| Apparent density | ISO60 | 0.83 g/cm³ | |
| melt mass-flow rate | ISO1133 | 2.0到5.0 g/10min | |
| Melt volume flow rate | ISO1133 | 1.50到4.00 cm³/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | Yield | ISO527-2 | 17.0 MPa |
| Flexural modulus | ISO178 | 370 MPa | |
| Bending stress | ISO178 | 9.00 MPa | |
| TensileStrength | ISO527 | >300 % | |
| Tensile modulus | ISO527-2 | 390 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179/1eA | 无断裂 | |
| Impact strength of simply supported beam without notch | ISO179/1eU | 无断裂 |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water vapor permeability | ISO15106-3 | 70 g/m²/24hr | |
| OxygenPermeability | ISO15105-2 | 850 cm³/m²/bar/24hr | |
| NitrogenPermeability | DIN53380-2 | 160 cm³/m²/bar/24hr |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO306/A | 89.0 °C | |
| ISO3146 | >155 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.