'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPO GFN1-701 SABIC INNOVATIVE JAPAN
155
Form：Granules | Grade：Injection grade
Properties:
High mobilityFlame retardantGlass fiber reinforcedHigh temperature resistan
Typical Applications:
household electrical appliancesAutomotive interior partsWater sports equipment
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | household electrical appliances | Automotive interior parts | Water sports equipment |
| Properties: | High mobility | Flame retardant | Glass fiber reinforced | High temperature resistan |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 21.7 | J |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 28 | kJ/m² |
| -30°C | ISO 180/1U | 25 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 11 | kJ/m² |
| -30°C | ISO 180/1A | 9.4 | kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 35 | kJ/m² |
| -30°C | ISO 179/1eU | 33 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.5mm | UL 94 | HB | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | Break | ISO 527-2 | 64.0 | Mpa |
| Break | ASTM D638 | 63.0 | Mpa | |
| Tensile modulus | ISO 527-2/1 | 4400 | Mpa | |
| ASTM D638 | 4350 | Mpa | ||
| elongation | Break | ASTM D638 | 3.0 | % |
| Tensile strain | Break | ISO 527-2 | 3.0 | % |
| Bending modulus | 50.0mmSpan4 | ASTM D790 | 3840 | Mpa |
| 100mmSpan5 | ASTM D790 | 3590 | Mpa | |
| ISO 178 | 4160 | Mpa | ||
| bending strength | ISO 178 | 122 | Mpa | |
| Yield,50.0mmSpan4 | ASTM D790 | 116 | Mpa | |
| Yield,100mmSpan5 | ASTM D790 | 108 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTM D648 | 131 | °C |
| RTI Imp | UL 746 | 90.0 | °C | |
| RTI Elec | UL 746 | 90.0 | °C | |
| RTI Str | UL 746 | 90.0 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,100mmSpan | ISO 75-2/Be | 132 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTM D648 | 122 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTM D648 | 125 | °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 124 | °C | |
| Vicat softening temperature | -- | ISO 306/B50 | 131 | °C |
| -- | ISO 306/B120 | 134 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 5.1E-05 | cm/cm/°C |
| TD：-40to40°C | ASTME831 | 7.1E-05 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Outdoor applicability | UL 746C | f1 | ||
| Water absorption rate | 24hr | ASTM D570 | 0.060 | % |
| Shrinkage rate | MD：3.20mm | Internal Method | 0.20-0.50 | % |
| Melt Volume Flow Rate (MVR) | 300°C/5.0kg | ISO 1133 | 16.4 | cm3/10min |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 17 | g/10min |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot wire ignition | HWI | UL 746 | PLC 5 | |
| High voltage arc tracing rate | HVTR | UL 746 | PLC 4 | |
| High arc combustion index | HAI | UL 746 | PLC 4 | |
| Arc resistance | ASTM D495 | PLC7 | ||
| Dissipation factor | 1MHz | ASTM D150 | 1.4E-03 | |
| Dielectric constant | 1MHz | ASTM D150 | 2.90 | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | L-Sale | ASTM D785 | 104 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.