Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 1.0 g/10min |
| Shrinkage rate | | STM640808 | 0.93 % |
| Shrinkage rate | | STM640808 | 0.56 % |
| water content | | ISO 960 | 0.15 % |
| density | | ISO 1183 | 1.46 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-13 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 14000 MPa |
| tensile strength | Yield | ISO 527-2 | 210 MPa |
| Tensile strain | Yield | ISO 527-2 | 2.0 % |
| Flexural modulus | | ISO 178 | 12000 MPa |
| bending strength | | ISO 178 | 290 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 12 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 13 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 70 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 75 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Volume resistivity | | IEC 60093 | 1E+17 ohms·cm |
| dielectric strength | | IEC 60243-1 | 90 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 240 °C |
| vicat | | ISO 306/B | 240 °C |
| melting temperature | | ISO 3146 | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.