Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238,ISO292 | 20 g/10min |
| Shrinkage rate | | ASTMD955 | 0.60到0.70 % |
| Shrinkage rate | | ASTMD955 | 0.60到0.70 % |
| Water absorption rate | | ASTMD570,ISO62 | 0.15 % |
| density | | ASTMD792,ISO1183 | 1.04 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 112 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Hot filament ignition temperature | | IEC60695-2-13 | 550 °C |
| Limiting Oxygen Index | | ASTMD2863 | <21 % |
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638,ISO527-2 | 2500 MPa |
| tensile strength | Yield | ASTMD638,ISO527-2 | 48.0 MPa |
| elongation | Break | ASTMD638,ISO527-2 | 25 % |
| Flexural modulus | | ASTMD790,ISO178 | 2400 MPa |
| Bending stress | | ISO178 | 66.0 MPa |
| Bending stress | Yield | ASTMD790 | 66.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179,ASTMD256 | 13 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256,ISO180 | 130 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648,ISO75-2/A | 85.0 °C |
| Continuous use temperature | | UL746B | 60.0 °C |
| vicat | | ASTMD15255,ISO306/A505 | 105 °C |
| vicat | | ASTMD15256,ISO306/B506 | 95.0 °C |
| BallPressure Test | | VDE0470 | 通过 |
| | ASTMD696 | 9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare