Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | g/cm³ | 1.15 -- |
Water absorption rate | | % | 2.2 -- |
Water absorption rate | | % | 7.0 -- |
hardness | Test Condition | Test Method | Test Result |
---|
ball-indentation hardness | | MPa | 175 150 |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | MPa | 3800 3000 |
tensile strength | Yield | MPa | 100 80.0 |
tensile strength | Break | MPa | 150 70.0 |
Tensile strain | Break | % | >15 -- |
Flexural modulus | | MPa | 3700 2800 |
compression stress | | MPa | 56.0 -- |
compression stress | | MPa | 79.0 -- |
compression stress | | MPa | 108 -- |
coefficient of friction | Steel - Dynamic | | 0.040 0.080 |
coefficient of friction | Steel - Static | | 0.35 -- |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | kJ/m² | >2.5 >12 |
Suspended wall beam without notch impact strength | | | 无断裂 |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Surface Resistivity | | ohms | 1E+12 1E+10 |
dielectric strength | | kV/mm | 50 20 |
dielectric constant | | | 3.70 -- |
Dissipation Factor | | | 0.030 -- |
Thermal performance | Test Condition | Test Method | Test Result |
---|
thermal conductivity | | W/m/K | 0.25 -- |
Heat distortion temperature | | °C | 210 -- |
Heat distortion temperature | | °C | 120 -- |
melting temperature | | °C | 220 -- |
Linear coefficient of thermal expansion | | cm/cm/°C | 7.0E-5到8.0E-5 -- |
specific heat | | J/kg/°C | 1670 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.