Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.28 g/cm³ |
| Shrinkage rate | | ISO294-4 | 0.50 % |
| Shrinkage rate | | ISO294-4 | 0.20 % |
| Humidity Absorption | | ISO1110 | 2.1 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| FlameRating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO1172 | 30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Break | ISO527-2/5 | 200 MPa |
| Tensile strain | Break | ISO527-2/5 | 2.0 % |
| Flexural modulus | | ISO178 | 18000 MPa |
| Bending stress | | ISO178 | 290 MPa |
| Fracture bending strain | | ISO178 | 2.0 % |
| Tensile modulus | | ISO527-2/1 | 23000 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 52 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 55 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+03 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | DINEN11357-1 | 220 °C |
| | ISO75-2/A | 210 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.