Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 0.950 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 17to27 g/10min |
| Shrinkage rate | | 内部方法 | <4.0 % |
| Shrinkage rate | | 内部方法 | <0.50 % |
| Water absorption rate | | ISO 62 | <0.10 % |
| gel content | | 内部方法 | >80 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | >91.0 % |
| UVCutoff-Wavelength | | 内部方法 | 360 nm |
| refractive index | | ISO 489 | 1.490 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| adhesion | | ASTM D903 | >8.0 kN/m |
| adhesion | | ASTM D903 | >10.0 kN/m |
| film | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-3 | 5.00 MPa |
| tensile strength | | ISO 527-3 | 15.0 MPa |
| elongation | Break | ISO 527-3 | >500 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D150 | >1.0E+14 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ASTM D148 | 65.0to75.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.