PLA TRANSMARE® BIO M106
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.25 g/cm³ | |
| melt mass-flow rate | ISO1133 | 20 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO868 | 70 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO180/1A | 3.0 kJ/m² | |
| Charpy Notched Impact Strength | ISO179/1A | 5.0 kJ/m² | |
| Impact strength of cantilever beam gap | ISO180/1A | 4.0 kJ/m² | |
| ISO180/1A | 5.5 kJ/m² | ||
| ISO180/1A | 6.4 kJ/m² | ||
| Charpy Notched Impact Strength | ISO179/1A | 2.5 kJ/m² | |
| ISO179/1A | 3.3 kJ/m² | ||
| ISO179/1A | 4.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| TensileStrain | ISO527-2/50 | 2.7 % | |
| Tensile strain | ISO527-2/50 | 15 % | |
| Flexural modulus | Injection | ISO178 | 2300 MPa |
| bending strength | ISO178 | 37.0 MPa | |
| Tensile modulus | ISO527-2/50 | 2600 MPa | |
| tensile strength | ISO527-2/50 | 49.0 MPa | |
| Tensile stress | ISO527-2/50 | 16.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO75-2/B | 50.0 °C | |
| ISO75-2/A | 48.0 °C | ||
| vicat | ISO306/A | 57.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.