Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.65 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.25 % |
| Shrinkage rate | | ASTM D955 | 0.90 % |
| Water absorption rate | | ASTM D570 | 0.030 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 122 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTM D638 | 184 MPa |
| elongation | Break | ASTM D638 | 1.7 % |
| Flexural modulus | | ASTM D790 | 12700 MPa |
| bending strength | Yield | ASTM D790 | 235 MPa |
| Tensile modulus | | ASTM D638 | 13700 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 84 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D150 | 4.00 |
| dielectric constant | | ASTM D150 | 4.00 |
| Dissipation Factor | | ASTM D150 | 1.5E-03 |
| Dissipation Factor | | ASTM D150 | 1.4E-03 |
| arc resistance | | ASTM D495 | 104 sec |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 4 |
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 12 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 260 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 8E-06 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6.3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare