PC ENH2900 8A9D020 SABIC INNOVATIVE NANSHA

Form：Granules | Grade：Injection grade

Properties:

Thermal stabilityHigh gloss

Typical Applications:

household electrical appliancesCastersElectrical applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	household electrical appliances \| Casters \| Electrical applications
Properties:	Thermal stability \| High gloss

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	65.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.1 mm	UL 94	V-1
	UL flame retardant rating	1.5 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	2.5 mm	UL 94	5VB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	2480	Mpa
tensile strength	Yield	ASTM D638	63.0	Mpa
tensile strength	tensile strength	Break	ASTM D638	42.0	Mpa
elongation	Yield	ASTM D638	4.0	%
elongation	elongation	Break	ASTM D638	65	%
Bending modulus	50.0 mm Span	ASTM D790	2240	Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	89.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80 to 90	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.040	%
Suggested injection volume			30 to 80	%
Temperature at the rear of the barrel			220 to 255	°C
Temperature in the middle of the barrel			220 to 265	°C
Temperature at the front of the material cylinder			245 to 275	°C
Spray nozzle temperature			245 to 275	°C
Processing (melt) temperature			245 to 275	°C
Mold temperature			60 to 80	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
Exhaust hole depth			0.038 to 0.076	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	78.0	°C
Vicat softening temperature		ASTM D15255	102	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	266°C/5.0 kg	ASTM D1238	26	g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.80	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.