POM F20-03 PTM NANTONG

Form：Granules | Grade：Injection grade

Properties:

Thermal stabilitywear resistantHigh temperature resistancurrency

Typical Applications:

Thermal stabilitywear resistantHigh temperature resistancecurrency

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Thermal stability \| wear resistant \| High temperature resistance \| currency
Properties:	Thermal stability \| wear resistant \| High temperature resistan \| currency

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	250	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	7.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	90.0	Mpa
Bending modulus		ISO 178	2600	Mpa
Nominal tensile fracture strain		ISO 527-2	30	%
Tensile strain	Yield	ISO 527-2	8.5	%
tensile strength	Yield	ISO 527-2	64.0	Mpa
Tensile modulus		ISO 527-2	2900	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1.1E-04	cm/cm/°C
Melting temperature		ISO 11357-3	166	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	100	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	156	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.41	g/cm³
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.22	%
Shrinkage rate	MD：3.00mm		2.0	%
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	7.70	cm3/10min
melt mass-flow rate	190°C/2.16kg	ISO 1133	9.0	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	IEC 60250	7E-03
Compared to the anti leakage trace index		IEC 60112	PLC 0
Dissipation factor	100Hz	IEC 60250	2E-03
Relative permittivity	1MHz	IEC 60250	3.90
Relative permittivity	Relative permittivity	100Hz	IEC 60250	3.90
Dielectric strength	3.00mm	IEC 60243-1	19	KV/mm
Dielectric strength	Dielectric strength	1.00mm	IEC 60243-1	32	KV/mm
Volume resistivity		IEC 60093	1E+14	ohms·cm
Surface resistivity		IEC 60093	1E+16	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.