PBT+PET TechnoDur PBT/PET GF 15 Natural (9972) TECHNOCOMPOUND GERMANY

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	35 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	35 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	6.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	Internal Method	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	750 °C

mechanical properties	Test Condition	Test Method	Test Result
Bending strain		ISO 178	4.5 %
bending strength	3.5%Strain	ISO 178	160 MPa
bending strength	bending strength	--	ISO 178	155 MPa
Bending modulus		ISO 178	5000 MPa
tensile strength	Break	ISO 527-2/5	110 MPa
Tensile modulus		ISO 527-2/1	6100 MPa
Tensile strain	Break	ISO 527-2/5	3.0 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	190 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	210 °C
Linear coefficient of thermal expansion	MD:23to80°C	ISO 11359-2	3E-05 cm/cm/°C
Melting temperature		ISO 11357-3	220to255 °C
Vicat softening temperature		ISO 306/B50	200 °C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	65.0 °C
Linear coefficient of thermal expansion	TD:23to80°C	ISO 11359-2	8E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation,23°C	ISO 62	0.40 %
Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	0.20 %
Shrinkage rate	MD	ISO 2577	0.35 %
Shrinkage rate	Shrinkage rate	TD	ISO 2577	1.2 %
Melt Volume Flow Rate (MVR)	265°C/2.16kg	ISO 1133	20.0 cm³/10min
density		ISO 1183	1.43 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Relative permittivity	1MHz	IEC 60250	3.60
Surface resistivity		IEC 60093	1E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dielectric strength	1.00mm	IEC 60243-1	26 kV/mm
Relative permittivity	100Hz	IEC 60250	3.80
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 2

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	190 MPa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.