| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 2577 | 0.10to0.20 % |
| Shrinkage rate | | ISO 2577 | 1.2to1.6 % |
| Shrinkage rate | | ISO 2577 | 0.10to0.20 % |
| Water absorption rate | | ISO 62 | 0.50 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| density | | ISO 1183 | 1.20 g/cm³ |
| Apparent density | | ISO 60 | 0.70 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 13.0 cm³/10min |
| Shrinkage rate | | ISO 2577 | 1.2to1.6 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 85.0 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 650 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 20 % |
| Burning rate - US-FMVSS | | ISO 3795 | passed |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| electrolytic corrosion | | IEC 60426 | A1 |
| GottfertMeltViscosity | | 内部方法 | 640 Pa·s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending Strain | | ISO 178 | 5.0 % |
| Tensile modulus | | ISO 527-2/1 | 1800 MPa |
| tensile strength | | ISO 527-2/50 | 40.0 MPa |
| tensile strength | | ISO 527-2/50 | 35.0 MPa |
| Tensile strain | | ISO 527-2/50 | 4.0 % |
| Nominal tensile fracture strain | | ISO 527-2/50 | >50 % |
| Tensile creep modulus | | ISO 899-1 | 1500 MPa |
| Tensile creep modulus | | ISO 899-1 | 1200 MPa |
| Flexural modulus | | ISO 178 | 1700 MPa |
| bending strength | | ISO 178 | 63.0 MPa |
| bending strength | | ISO 178 | 54.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ISO 180 | NoBreak |
| Charpy Notched Impact Strength | | ISO 179/1eA | 69 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | | ISO 180/A | 47 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/A | 66 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Surface Resistivity | | IEC 60093 | >1.0E+17 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+17 ohms·cm |
| relative permittivity | | IEC 60250 | 3.10 |
| relative permittivity | | IEC 60250 | 2.90 |
| Dissipation Factor | | IEC 60250 | 2.3E-03 |
| Dissipation Factor | | IEC 60250 | 0.014 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 91.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 60.0 °C |
| thermal conductivity | | ISO 8302 | 0.20 W/m/K |
| vicat | | ISO 306/B120 | 119 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.