Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.87 g/cm³ |
| Water absorption rate | | ASTM D570 | <0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Barcol Hardness | | ASTM D2583 | 75 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Thermal Gravimetric Analysis | | | Norecordableweightloss |
| Thermal-oxidativeDeterioration | | | 0.20 % |
| Space stability, shrinkage | | | 0.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 82.7 MPa |
| Flexural modulus | | ASTM D790 | 15900 MPa |
| Flexural modulus | | ASTM D790 | 14500 MPa |
| Flexural modulus | | ASTM D790 | 15200 MPa |
| bending strength | | ASTM D790 | 207 MPa |
| bending strength | | ASTM D790 | 214 MPa |
| bending strength | | ASTM D790 | 221 MPa |
| CompressiveStrength-Open-Hole | | ASTM D648 | Passed |
| tensile strength | | ASTM D638 | 75.8 MPa |
| tensile strength | | ASTM D638 | 75.8 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 800 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | 270 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.4E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.