Polyester XYLEX™ X8409AC resin
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO62 | 0.37 % | |
| ISO62 | 0.13 % | ||
| density | ASTMD792 | 1.20 g/cm³ | |
| ISO1183 | 1.20 g/cm³ | ||
| melt mass-flow rate | ASTMD1238 | 4.8 g/10min | |
| Melt volume flow rate | ISO1133 | 3.80 cm³/10min | |
| Shrinkage rate | 内部方法 | 0.50to0.80 % | |
| 内部方法 | 0.50to0.80 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | ASTMD1003 | 88.0 % | |
| Haze ratio | ASTMD1003 | 1.5 % | |
| refractive index | ASTMD542 | 1.576 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Break | ASTMD638 | 55.0 MPa |
| Tensile stress | Break | ISO527-2/50 | 60.0 MPa |
| elongation | Yield | ASTMD638 | 6.0 % |
| Tensile strain | Yield | ISO527-2/50 | 5.8 % |
| elongation | Break | ASTMD638 | 92 % |
| Tensile strain | Break | ISO527-2/50 | 120 % |
| Flexural modulus | ASTMD790 | 2220 MPa | |
| Tensile modulus | ASTMD638 | 2370 MPa | |
| ISO527-2/1 | 2180 MPa | ||
| Flexural modulus | ISO178 | 2000 MPa | |
| bending strength | ISO178 | 89.0 MPa | |
| ASTMD790 | 94.0 MPa | ||
| tensile strength | Yield | ASTMD638 | 57.0 MPa |
| Tensile stress | Yield | ISO527-2/50 | 60.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179/1eA | 8.0 kJ/m² | |
| Impact strength of cantilever beam gap | ASTMD256 | 200 J/m | |
| ASTMD256 | 850 J/m | ||
| ISO180/1A | 8.0 kJ/m² | ||
| ISO180/1A | 8.0 kJ/m² | ||
| ISO180/1A | 10 kJ/m² | ||
| Dart impact equipped with measuring instruments | ASTMD3763 | 70.0 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTMD648 | 116 °C | |
| ASTMD648 | 104 °C | ||
| ISO75-2/Ae | 102 °C | ||
| vicat | ASTMD152510 | 123 °C | |
| ISO306/B50 | 121 °C | ||
| ISO306/B120 | 123 °C | ||
| ASTME831 | 1E-04 cm/cm/°C | ||
| ISO11359-2 | 1E-04 cm/cm/°C | ||
| ISO11359-2 | 6E-05 cm/cm/°C | ||
| ASTME831 | 1E-04 cm/cm/°C | ||
| ISO11359-2 | 1E-04 cm/cm/°C | ||
| ISO11359-2 | 7E-05 cm/cm/°C | ||
| thermal conductivity | ISO8302 | 0.23 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.