Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.13 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 13 g/10min |
| Shrinkage rate | | ASTM D955 | 0.30to0.50 % |
| Water absorption rate | | ISO 62 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Hardness (Rockwell) | | ISO 2039-2 | 80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 2.0 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 15 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2 | 70.0 MPa |
| Flexural modulus | | ISO 178 | 3400 MPa |
| bending strength | | ISO 178 | 115 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ASTM D648 | 90.0 °C |
| Hot deformation temperature (HDT) | | ISO 75-2/A | 80.0 °C |
| | ISO 11359-2 | 7E-05 cm/cm/°C |
| BallPressure Test | | | 90 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.