PP Fiberfil® J-60/20/H Canada Fiberfil

Properties:
Filler glass fiber reinforced material 20% filler by weight
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	64 J/m

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ASTM D638	4140 MPa
bending strength	23°C	ASTM D790	93.1 MPa
Bending modulus	23°C	ASTM D790	3790 MPa
elongation	Yield,23°C	ASTM D638	3.5 %
tensile strength	23°C	ASTM D638	68.9 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	149 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	157 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	24hr	ASTM D570	0.030 %
Shrinkage rate	MD：6.35mm	ASTM D955	0.40 %
Shrinkage rate	Shrinkage rate	MD：3.18mm	ASTM D955	0.30 %
melt mass-flow rate	230°C/2.16kg	ASTM D1238	5.0 g/10min
density		ASTM D792	1.04 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	100to110

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.