ABS TAIRILAC® AX4300 FCFC TAIWAN
130
- Properties:Moderate heat resistanceHeat resistanceHigh impact resistance
- Usages:Automotive sector
- Certificates:MSDSTDSProcessingMSDSULRoHSSVHCEnvironmental
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | 23℃ | FCFC Method | 0.4-0.7 | |
| Melt mass flow rate | 220℃×10kgf(98N) | ASTM D-1238(ISO 1133) | 5.5 | g/10min |
| density | 23℃/23℃ | ASTM D-792(ISO 1183) | 1.05 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 23℃ | ASTM D-638(ISO 527) | 430(42) | kg/m2(MPa) |
| Rockwell hardness | 23℃ | ASTM D-785(ISO 2039/2) | R-103 | |
| Bending modulus | 23℃ | ASTM D-790(ISO 178) | 21000(2050) | kg/m2(MPa) |
| bending strength | 23℃ | ASTM D-790(ISO 178) | 720(71) | kg/m2(MPa) |
| IZOD impact strength | 23℃，1/4” | ASTM D-256(ISO R180) | 30(294) | kg.cm/cm(J/m) |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | 1Kg load | ASTM D-1525(ISO 306) | 119 | |
| Hot deformation temperature | Annealed(95℃×8Hr) | |||
| Unanneaied 18.6kg/cm²(1/2"厚) | ASTM D-648(ISO 75/A) | 100 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.