AES DIALAC® SK50 UMG JAPAN
501
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 220℃/2.16 kg | ISO 1133 | 17.0 | cm3/10min |
| Shrinkage rate | MD，23℃ | ISO 294-4 | 0.70 到 0.90 | % |
| Melt Volume-Flow Rate (MVR) | 220°C/10.0kg | ISO1133 | 17.0 | cm3/10min |
| Shrinkage rate | MD：23°C | ISO294-4 | 0.70到0.90 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO2039-2 | 100 | |
| Tensile modulus | 23°C | ISO527-2 | 2050 | Mpa |
| tensile strength | 23°C | ISO527-2 | 42.0 | Mpa |
| Bending modulus | 23°C | ISO178 | 2200 | Mpa |
| bending strength | 23°C | ISO178 | 65.0 | Mpa |
| Rockwell hardness | 23℃ | ISO 2039-2 | 100 | R 计秤 |
| Tensile modulus | 23℃ | ISO 527-2 | 2050 | Mpa |
| tensile strength | 23℃ | ISO 527-2 | 42.0 | Mpa |
| Bending modulus | 23℃ | ISO 178 | 2200 | Mpa |
| bending strength | 23℃ | ISO 178 | 65.0 | Mpa |
| Impact strength of simply supported beam gap | -30℃ | ISO 179 | 8.0 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.80MPa，未退火 | ISO 75-2/Af | 78.0 | °C |
| 1.8MPa,未退火 | ISO75-2/Af | 78.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
| Linear expansion coefficient | 流动 | ISO 11359-2 | 0.000090 | cm/cm/℃ |
| Flame retardant grade | 1.50mm | UL 94 | HB |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.