HIPS 641F
0
- Properties:High impact resistanceheat resistanceand good demolding performance
- Usages:Electrical and electronic application fieldsvideo tapestelevision casingsautomotive internal parts
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.04 g/cm3 | |
| Melt volume flow rate | ISO 1133 | 2.50 cm3/10min | |
| Shrinkage rate | ISO 294-4 | 0.50-0.70 % | |
| Water absorption rate | ISO 62 | <0.10 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 90.0 MPa | |
| Tensile modulus | ISO 527-2 | 2000 MPa | |
| tensile strength | Yield | ISO 527-2/50 | 28.0 MPa |
| Break | 27.0 | ||
| Tensile strain | Yield | ISO 527-2/50 | 1.7 % |
| elongation at break | ISO 527-2/50 | 40 % | |
| bending strength | ISO 178 | 44.0 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 14 kJ/m2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/B50 | 96.0 ℃ | |
| Linear coefficient of thermal expansion | DIN 53752 | 0.000080 cm/cm./℃ | |
| Heat distortion temperature | ISO 75-2/A | 88.0 ℃ | |
| thermal conductivity | DIN 42612 | 0.16 W/m/k |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.