PP Homopolymer Tecnoprene® A60K4 NAT001 SO.F.TER ITALY

Properties:

Filler glass fiber reinforced material 20% filler by weight

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

Filler | glass fiber reinforced material | 20% | filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ASTM D256	120	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-20°C	ASTM D256	90	J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	11	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.2mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D790	115	MPa
Bending modulus		ASTM D790	4300	MPa
tensile strength	Break	ASTM D638	75.0	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ASTM D696	6.5E-05	cm/cm/°C
Vicat softening temperature		ASTM D15252	128	°C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	145	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230°C/2.16kg	ASTM D1238	3.8	g/10min
Shrinkage rate		Internal Method	0.70	%
Water absorption rate	23°C,24hr	ASTM D570	0.020	%
density		ASTM D792	1.04	g/cm³
ash content		Internal Method	20	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	1kHz	ASTM D150	2.40
Surface resistivity		ASTM D257	1E+15	ohms
Compared to the anti leakage trace index		IEC 60112	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.