PP 3720E 10000
8
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Mold shrinkage rate | SABIC method | 1.1 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 18 g/10min | |
| density | ISO 1183 | 1.04 g/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy notch impact strength | ISO 179/1eA | 6 KJ/m | |
| Charpy without notch impact strength | ISO 179/1eU | 18 KJ/m | |
| hardness | ISO 868 | 71 | |
| Yield tensile strength | ISO 527 | 28 Mpa | |
| Tensile strength at break | ISO 527 | 25 Mpa | |
| elongation | ISO 527 | 45 % | |
| Flexural modulus | ASTM D-790 | 2200 Mpa | |
| IZOD notch impact strength | ISO 180/4A | 6 KJ/m | |
| ISO 180/4A | 3.5 KJ/m | ||
| ISO 180/4A | 3 KJ/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTM D-696 | 110 µm/mK | ||
| ASTM D-696 | 80 µm/mK | ||
| ISO 75/B | 110 °C | ||
| vicat | ISO 306/A | 145 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.