HIPS Bycolene® 2710
463
- Properties:Low temperature resistancHigh temperature resistanhigh strengthHigh impact resistanceResistance to stress crac
- Usages:sheetPlate
- Certificates:UL
CompareTechnical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Color | 钛白 | ||
| purpose | 板材 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 10 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 120 kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | NB kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 7 kg·cm/cm(J/M)ft·lb/in | ||
| Tensile modulus | ASTM D638/ISO 527 | 1600 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 1500 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 32 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.05 | |
| Shrinkage rate | ASTM D955 | 0.40-0.70 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 5 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | <0.1 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | 94HB | |
| Heat distortion temperature | ASTM D648/ISO 75 | 82 ℃（℉） | |
| vicat | ASTM D1525/ISO R306 | 92 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.