Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 0.960 g/cm³ |
| Water absorption rate | | ISO 62 | 0.010 % |
| molecular weight distribution | | | 500000 g/mol |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 64 |
| ball-indentation hardness | | ISO 2039-1 | 45.0 MPa |
| Shore hardness | | ISO 868 | 66 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | <20 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Relative Weight Loss | | 内部方法 | 350 |
| Relative Weight Loss | | 内部方法 | 1600 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Nominal tensile fracture strain | | ISO 527-2/1B/50 | >50 % |
| Tensile modulus | | ISO 527-2/1B/1 | 1300 MPa |
| tensile strength | Yield | ISO 527-2/1B/50 | 28.0 MPa |
| Tensile strain | Yield | ISO 527-2/1B/50 | 10 % |
| compression stress | | ISO 604/1 | 9.00 MPa |
| compression stress | | ISO 604/1 | 14.5 MPa |
| compression stress | | ISO 604/1 | 22.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | 内部方法 | >20 kJ/m² |
| Charpy Notched Impact Strength | Partial Break | ISO 179/1eA | 85 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 11357-3 | 130to135 °C |
| Linear coefficient of thermal expansion | | | 1.5E-04 cm/cm/°C |
| thermal conductivity | | | 0.40 W/m/K |
| Minimum operating temperature | | | -60 °C |
| Continuous use temperature | | | 80.0 °C |
| Continuous use temperature | | | 120 °C |
| vicat | | ISO 306/B | 80.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 44.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.