Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 18 g/10min |
| Melt volume flow rate | | ISO 1133 | 15.0 cm3/10min |
| Shrinkage rate | | 内部方法 | 0.88-0.94 % |
| Shrinkage rate | | 内部方法 | 0.95-1.0 % |
| Water absorption rate | | ISO 62 | 3.8 % |
| Water absorption rate | | ISO 62 | 0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-1 |
| UL flame retardant rating | | UL 94 | 5VB5VA |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 825 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 88.0 Mpa |
| tensile strength | | ISO 527-2/5 | 88.0 Mpa |
| tensile strength | | ASTM D638 | 88.0 Mpa |
| tensile strength | | ISO 527-2/5 | 88.0 Mpa |
| Tensile strain | | ISO 527-2/5 | 3.0 % |
| Tensile strain | | ISO 527-2/5 | 3.0 % |
| Flexural modulus | | ASTM D790 | 4600 Mpa |
| Flexural modulus | | ISO 178 | 4600 Mpa |
| bending strength | | ISO 178 | 145 Mpa |
| bending strength | | ASTM D790 | 145 Mpa |
| Tensile modulus | | ASTM D638 | 5000 Mpa |
| Tensile modulus | | ISO 527-2/1 | 5000 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 5.0 kJ/m² |
| Dart impact | | ASTM D3763 | 12.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 23 KV/mm |
| dielectric strength | | ASTM D149 | 24 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 1 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 220 °C |
| Heat distortion temperature | | ISO 75-2/Bf | 224 °C |
| vicat | | ASTMD152511 | 218 °C |
| vicat | | ISO 306/B120 | 220 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 4.1E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 7.4E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.