Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO294-4 | 1.2 % |
| Shrinkage rate | | ISO294-4 | 0.85 % |
| Water absorption rate | | ISO62 | 1.5 % |
| Water absorption rate | | ISO62 | 0.80 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ElectrolyticalCorrosion | | IEC60426 | A1 |
| ISO Shortcut | | ISO1874 | PA12,KH,18-010 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 1350 Mpa |
| Tensile stress | | ISO527-2 | 45.0 Mpa |
| Tensile strain | | ISO527-2 | 5.0 % |
| Tensile strain | | ISO527-2 | >50 % |
| elongation at break | | ASTM D412/ISO 527 | >50 % |
| Tensile modulus | | ASTM D412/ISO 527 | 1350 kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D412/ISO 527 | 5 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 27 KV/mm |
| | IEC60250 | 3.80 |
| | IEC60250 | 2.50 |
| Dissipation Factor | | IEC60250 | 0.045 |
| Dissipation Factor | | IEC60250 | 0.031 |
| CTI | | IEC60112 | 600 V |
| CTI | | IEC60112 | >600 V |
| Volume resistivity | | ASTM D257/IEC 60093 | 10^15 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.01 kg·cm/cm(J/M)ft·lb/in |
| Water absorption rate | | ASTM D570/ISO 62 | 1.5 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 50.0 °C |
| vicat | | ISO306/A | 170 °C |
| vicat | | ISO306/B | 140 °C |
| melting temperature | | ISO11357-3 | 178 °C |
| | ISO11359-2 | 1.5E-04 cm/cm/°C |
| | ISO75-2/B | 110 °C |
| | ASTM D648/ISO 75 | 50 ℃（℉） |
| | ASTM D648/ISO 75 | 110 ℃（℉） |
| melting point | | | 178 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.