PA66 70G35HSL NC DUPONT USA

Form：Granules | Grade：Enhanced level

Properties:

Thermal stabilityFiller: Glass fiber reinf35%Filler by weight35%Filler by weight

Typical Applications:

sporting goodsElectrical applications

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	sporting goods \| Electrical applications
Properties:	Thermal stability \| Filler: Glass fiber reinf \| 35% \| Filler by weight \| 35% \| Filler by weight

Certificates

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	23°C	ISO 527-2	210	Mpa
Elongation at Break	23°C	ISO 527-2	3.20	%
Tensile modulus	23°C	ISO 527-2	11200	Mpa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	15	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	12	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	Melting Temperature	ISO 11357-3	262	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1E-04	cm/cm/°C
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	261	°C
Hot deformation temperature	Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	252	°C
Vicat softening temperature		ISO 306/B50	255	°C
Vicat softening temperature	Vicat softening temperature	玻璃转化温度	ISO 11357-2	80	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.41	g/cm³
Shrinkage rate	MD2.0mm	ISO 294-4	0.30	%
Shrinkage rate	Shrinkage rate	TD2.0mm	ISO 294-4	1.10	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1E+13	Ω.cm
Dielectric strength		IEC 60243-1	33	KV/mm
Dissipation factor	相对漏电起痕指数	IEC 60112	400	V
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ISO 2039-2	105	M（Scale）
Rockwell hardness	Rockwell hardness		ISO 2039-2	125	R
flame retardant performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL -94	HB	0.71mm
	UL flame retardant rating		UL -94	HB	1.50mm
	UL flame retardant rating	UL flame retardant rating		UL -94	HB	3.00mm
Extreme Oxygen Index		ISO 4589-2	24	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 70G35HSL NC DUPONT USA

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index