Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.43 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 1.5 % |
| Shrinkage rate | | ISO 294-4 | 1.5 % |
| Water absorption rate | | ISO 62 | 2.4 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | UL 94 | V-0 |
| Flammability level | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 3400 Mpa |
| tensile strength | | ISO 527-2 | 80.0 Mpa |
| Nominal tensile fracture strain | | ISO 527-2 | 7.0 % |
| Flexural modulus | | ISO 178 | 3200 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 3.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 4.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 30 KV/mm |
| relative permittivity | | IEC 60250 | 3.80 |
| relative permittivity | | IEC 60250 | 3.50 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 190 °C |
| melting temperature | | ISO 11357-3 | 295 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8.0E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 9.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.