PA6 6FL BK
45
- Properties:standard
- Usages:Automotive sectorElectric wireCable
Compare
View PricesTechnical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| notes | 代替B3S、B30S、1013B、CM1017、F223-D | ||
| 润滑PA6.用于高温时不至迅速变脆。受热寿命最佳.电器性能良好 | |||
| Color | 黑色 | ||
| purpose | 马达之定子、线圈骨架、需要较高使用温度的电子电器零件 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 45 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 6 kg·cm/cm(J/M)ft·lb/in | ||
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 5 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 12 % | |
| Tensile modulus | ASTM D638/ISO 527 | 2800 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 65 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 120 | |
| Flexural modulus | ASTM D790/ISO 178 | 2000 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 105 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.13 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 90 g/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 1.0E+13 Ω | |
| Volume resistivity | ASTM D257/IEC 60093 | 1.0E+15 Ω.cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Hot deformation temperature (HDT) | ASTM D648/ISO 75 | 170 ℃（℉） | |
| ASTM D648/ISO 75 | 75 ℃（℉） | ||
| melting temperature | 222 ℃（℉） | ||
| vicat | ASTM D1525/ISO R306 | 205 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.