Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 10 g/10min |
| Shrinkage rate | | ISO 294-4 | 0.50to0.70 % |
| Water absorption rate | | ASTM D570 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO 2039-2 | 80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ISO 178 | 93.0 MPa |
| tensile strength | Break | ISO 527-2 | 70.0 MPa |
| Tensile strain | Break | ISO 527-2 | 120 % |
| Flexural modulus | | ISO 178 | 2230 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 57 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 4E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 16 kV/mm |
| arc resistance | | ASTM D495 | 120 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 140 °C |
| Heat distortion temperature | | ISO 75-2/A | 132 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.