LLDPE R50035E SABIC SAUDI

Form：Granules | Grade：Rotational molding grade

Properties:

Resistance to stress cracHigh toughness

Typical Applications:

Industrial applicationsRigid package

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Industrial applications \| Rigid package
Properties:	Resistance to stress crac \| High toughness

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			高环境应力开裂性和韧性、低的扭曲性
purpose			家用器皿
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D-1238	5.0	g/10min
density		ASTM D-1505	0.935
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Secant modulus	延长，1%Strain	ASTM D-790	500	Mpa
tensile strength	Yield	ASTM D-638	18	Mpa
tensile strength	tensile strength	Break	ASTM D-638	11.5	Mpa
elongation	Break	ASTM D-638	700	%
bending strength		ASTM D-790	19.3	Mpa
Bending modulus		ASTM D-790	724	Mpa
Shore hardness		ASTM D-2240	69
Environmental stress cracking resistance	100%Igepal,F50	ASTM D-1693A	＞300	hrs
Elongation at Break		ASTM D638/ISO 527	700	%
Tensile modulus		ASTM D638/ISO 527	19.3	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	18	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	724	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D-1525	115	°C
Brittle temperature		ASTM D-746	＜-75	°C
Vicat softening temperature		ASTM D1525/ISO R306	115	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	0.935
melt mass-flow rate		ASTM D1238/ISO 1133	5	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.