Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.46 -- |
| Shrinkage rate | | % | 0.80to1.0 -- |
| Water absorption rate | | % | 0.90to1.0 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 118 105 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-2 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | MPa | 155 100 |
| Tensile modulus | | MPa | 6700 3500 |
| tensile strength | | MPa | 85.0 65.0 |
| elongation | Break | % | 1.0 32 |
| Flexural modulus | | MPa | 5800 3200 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 50 90 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+12 -- |
| dielectric strength | | kV/mm | 15 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 185 -- |
| Heat distortion temperature | | °C | 135 -- |
| Continuous use temperature | | °C | 90.0to100 -- |
| melting temperature | | °C | 214to220 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare