Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 1.1 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| Water absorption rate | | ISO 62 | 5.7 % |
| Water absorption rate | | ISO 62 | 1.8 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO 3795 | 28 mm/min |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| FMVSS combustion rate | | FMVSS 302 | B |
| 雾化 - G-value (condensate) | | ISO 6452 | 6.0E-4 g |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 11000 Mpa |
| tensile strength | | ISO 527-2 | 200 Mpa |
| Tensile strain | | ISO 527-2 | 3.0 % |
| Flexural modulus | | ISO 178 | 9500 Mpa |
| bending strength | | ISO 178 | 280 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 75 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| Ejection Temperature | | | 210 °C |
| Emission of Organic Compounds | | VDA 277 | 10.0 µgC/g |
| Odor | | VDA 270 | 3.00 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 1 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| Drying time - hot air dryer | | | 2.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.20 % |
| Processing (melt) temperature | | | 275 to 295 °C |
| Melt Temperature, Optimum | | | 285 °C |
| Temperature | | | 70 to 120 °C |
| Mold Temperature, Optimum | | | 100 °C |
| pressure holding | | | 50.0 to 100 Mpa |
| pressure holding | | | yes |
| Hold Pressure Time | | | 3.00 s/mm |
| Maximum Screw Tangential Speed | | | 12 m/min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 261 °C |
| Heat distortion temperature | | ISO 75-2/A | 252 °C |
| melting temperature | | ISO 11357-3 | 262 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.8E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 2.4E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.3E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8.3E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 6.5E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.4E-4 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.