PA6 6G30FL
27
- Properties:enhanceGlass fiber reinforced
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.36 g/cm³ | |
| Shrinkage rate | ISO 2577 | 0.25-0.55 % | |
| Water absorption rate | ISO 62 | 6.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 122 | |
| Tensile modulus | ISO 527-2/1 | 8500 Mpa | |
| tensile strength | ISO 527-2/5 | 140 Mpa | |
| Tensile strain | ISO 527-2/5 | 3.0 % | |
| Flexural modulus | ISO 178 | 5800 Mpa | |
| Impact strength of cantilever beam gap | ISO 180/1A | 5.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| Volume resistivity | IEC 60093 | 1E+15 ohm.cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 205 °C | |
| vicat | ISO 306/B50 | 210 °C | |
| melting temperature | ISO 3146 | 220 °C | |
| Obstructive level | UL 94 | HB | |
| Heat distortion temperature | ISO 75-2/B | 215 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.