| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 收缩率 | TD | ISO294-4 | 0.40 % |
| 收缩率 | MD | ISO294-4 | 0.20 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 热变形温度 | 1.8MPa,未退火 | ISO75-2/A | 236 °C |
| 熔融温度 | | ISO11357-3 | 260 °C |
| 线性热膨胀系数 | MD：-- | ISO11359-2 | 1.4E-05 cm/cm/°C |
| 线性热膨胀系数 | MD：-40to23°C | ISO11359-2 | 1.7E-05 cm/cm/°C |
| 线性热膨胀系数 | TD：-- | ISO11359-2 | 5.5E-05 cm/cm/°C |
| 线性热膨胀系数 | TD：-40to23°C | ISO11359-2 | 5.5E-05 cm/cm/°C |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| 燃烧速率3 | 1.00mm | ISO3795 | 25 mm/min |
| UL阻燃等级 | 0.75mm | UL94 | HB |
| UL阻燃等级 | 1.5mm | UL94 | HB |
| UL阻燃等级 | 0.75mm | IEC60695-11-10,-20 | HB |
| UL阻燃等级 | 1.5mm | IEC60695-11-10,-20 | HB |
| 极限氧指数 | | ISO4589-2 | 27 % |
| FMVSS可燃性 | | FMVSS302 | B |
| 电气性能 | Test Condition | Test Method | Test Result |
|---|
| 体积电阻率 | | IEC60093 | 1E+15 ohms·cm |
| 漏电起痕指数 | | IEC60112 | 600 V |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 拉伸模量 | | ISO527-2 | 16500 Mpa |
| 拉伸应力 | 断裂 | ISO527-2 | 250 Mpa |
| 拉伸应变 | 断裂 | ISO527-2 | 2.8 % |
| 弯曲模量 | | ISO178 | 15000 Mpa |
| 泊松比 | | ISO527 | 0.38 |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|
| 简支梁无缺口冲击强度 | 23°C | ISO179/1eU | 95 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.