Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.84to1.98 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.020to0.050 % |
| Water absorption rate | | ASTM D570 | <0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CureTime | | | 40.0to50.0 sec |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 108to147 MPa |
| compressive strength | | ASTM D695 | 137to157 MPa |
| tensile strength | | ASTM D638 | 29.4to49.0 MPa |
| Flexural modulus | | ASTM D790 | 13700to17700 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 270to370 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | ASTM D495 | >180 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | >200 °C |
| melting temperature | | DSC | 116 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.