Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.92 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.32to0.37 % |
| Water absorption rate | | ASTM D570 | <0.10 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 49 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 12700to13700 MPa |
| bending strength | | ASTM D790 | 108to118 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1.0E+14到1.0E+15 ohms·cm |
| Volume resistivity | | ASTM D257 | 1.0E+13到1.0E+14 ohms·cm |
| dielectric strength | | ASTM D149 | 30to33 kV/mm |
| arc resistance | | ASTM D495 | 180 sec |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTM D696 | 3E-05 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 265 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.