Unspecified Techsil® VT2420LV
0
CompareTechnical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Curing Time | 4.0 hr | ||
| 24 hr | |||
| GelTime | 12 min | ||
| 30 min | |||
| surface drying time | 20 min | ||
| 120 min | |||
| STORAGE STABILITY | 6.0 min | ||
| 15 min | |||
| Color | Clear/Transparent | ||
| Clear/Transparent | |||
| MixRatiobyWeight(PBW) | 0.91 | ||
| 1.0 | |||
| MixRatiobyVolume(PBV) | 1.0 | ||
| 1.0 | |||
| density | 1.05 g/cm³ | ||
| 1.11 g/cm³ | |||
| 1.16 g/cm³ | |||
| Viscosity | 0.60 Pa·s | ||
| 0.70 Pa·s | |||
| 0.80 Pa·s | |||
| Curing Time | 2.0 hr |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 1.2 % | ||
| Shore hardness | 70 | ||
| tensile strength | 15.0 MPa | ||
| elongation | Break | 100 % | |
| compressive strength | <10.0 MPa | ||
| dielectric strength | 20 kV/mm |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | 1.470to1.480 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| operate temperature | -55-120 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | 1.0E-4到1.5E-4 cm/cm/°C | ||
| thermal conductivity | 0.25 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.