Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | 1.80 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strength at break | | ISO527 | 125 Mpa |
| elongation at break | | ISO527 | 3.5 % |
| Yield bending strength | | ISO178 | 195 Mpa |
| Flexural modulus | | ISO178 | 5000 Mpa |
| Charpy Notched Impact Strength | | ISO179 | 8 kJ/m² |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 65 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.27 g/cm³ |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ISO167 | 19600 Ω |
| dielectric strength | | IEC1183 | 20 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature 1.8MPa | | ISO76 | 185 ℃ |
| unknown | Test Condition | Test Method | Test Result |
|---|
| unknown | | | HB 厚度3.0mm/℃ |
| unknown | | | 0.7 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare