Technical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| MixRatiobyWeight(PBW) | | | 100 |
| MixRatiobyWeight(PBW) | | | 23 |
| MixRatiobyWeight(PBW) | | | 0.838 g/cm³ |
| Curing Time | | | 1.0到2.0 hr |
| Curing Time | | | 4.0到6.0 hr |
| Curing Time | | | 16到24 hr |
| MixRatiobyWeight(PBW) | | | 45 Pa·s |
| Curing Time | | | 30 min |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 0.10 % |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | | >1.0E+13 ohms·cm |
| Dissipation Factor | | | 0.050 |
| Water absorption rate | | | 0.40 % |
| Supporting hardness | | | 78 |
| tensile strength | | | 29.6 MPa |
| Compression Strength | | | 68.9 MPa |
| electric strength | | | 15 kV/mm |
| | | 2.90 |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting mixed viscosity | | | 5000 cP |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Operating | | | -65.0到105 °C |
| Outgassing | | | 0.0900 |
| Outgassing | | | 0.740 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | | 34.5 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | | 4.3E-05 cm/cm/°C |
| thermal conductivity | | | 0.19 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.