ABS H802 901510 INEOS STYRO THAILAND

Form：Granules

Typical Applications:

Application in the automotive fieldAutomotive External Parts

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:

Application in the automotive field | Automotive External Parts

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179	7.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	15	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	80	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	100	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	2700	Mpa
tensile strength	Yield,23°C	ISO 527-2	51.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2	2.8	%
Tensile strain	Tensile strain	Break,23°C	ISO 527-2	>15	%
Bending modulus		ISO 178	2700	Mpa
bending strength		ISO 178	80.0	Mpa
Ball Pressure Test		ISO 2039-1	115	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	107	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	101	°C
Vicat softening temperature		ISO 306/B50	109	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	8E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.05	g/cm³
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	8.00	cm3/10min
Shrinkage rate		ISO 294-4	0.40-0.70	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	1.50mm	IEC 60243-1	34	KV/mm
Relative permittivity	100Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.00
Dissipation factor	100Hz	IEC 60250	6E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.010
Compared to the anti leakage trace index		IEC 60112	PLC 0
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.