LDPE LD2420H PCC IRAN

Form：Granules

Properties:

Low speed solidification Low speed solidification optical performance Good processabilityNo additivesGeneral purpose

Typical Applications:

Food packagingFoamchipfilmFoamFood packagingShrinkable filmGeneral purpose

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Food packaging \| Foam \| chip \| film \| Foam \| Food packaging \| Shrinkable film \| General purpose
Properties:	Low speed solidification \| Low speed solidification \| optical performance \| Good processability \| No additives \| General purpose

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
gloss	20°, 50.0 μm, Blown Film	ASTM D2457	> 80
turbidity	50.0 μm, Blown Film	ASTM D1003	< 8.0	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	Compression Molded	ISO 527-2	260	Mpa
tensile strength	Yield, Compression Molded	ISO 527-2	11.0	Mpa
Film thickness - tested			50	µm
tensile strength	MD: Break, 50 μm, Blown Film	ISO 527-3	21.0	Mpa
tensile strength	tensile strength	TD: Break, 50 μm, Blown Film	ISO 527-3	20.0	Mpa
elongation	MD: Break, 50 μm, Blown Film	ISO 527-3	250	%
elongation	elongation	TD: Break, 50 μm, Blown Film	ISO 527-3	600	%
Dart impact	50 μm, Blown Film	ASTM D1709	90	g
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D1525	93.0	°C
Melting temperature		ISO 11357-3	111	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190℃/2.16 kg	ISO 1133	1.9	g/10 min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.