ASA XTWM206-BK1C091 SABIC INNOVATIVE US

189

Form：Granules | Grade：Injection grade

Properties:

ColorableWeather resistance

Typical Applications:

Electronic and electrical componentsLawn garden equipmentHigh temperature applications

Supplier(3)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electronic and electrical components \| Lawn garden equipment \| High temperature applications
Properties:	Colorable \| Weather resistance

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
gloss	60°, 无织构	ASTM D523	93
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	-30°C, Total Energy	ASTM D3763	3.00	J
Dart impact	Dart impact	23°C, Total Energy	ASTM D3763	36.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break5	ASTM D638	26	%
	elongation	Break	ISO 527-2/50	36	%
		elongation	Break6	ASTM D638	27	%
			elongation	Yield	ISO 527-2/50	2.8	%
				elongation	Yield5	ASTM D638	2.7	%
				elongation	elongation	Yield6	ASTM D638	2.5	%
tensile strength	Break	ISO 527-2/50	36.0	Mpa
	tensile strength	Break5	ASTM D638	37.0	Mpa
		tensile strength	Break6	ASTM D638	36.0	Mpa
			tensile strength	Yield	ISO 527-2/50	45.0	Mpa
				tensile strength	Yield6	ASTM D638	43.0	Mpa
				tensile strength	tensile strength	Yield5	ASTM D638	46.0	Mpa
Tensile modulus	--	ISO 527-2/1	2350	Mpa
	Tensile modulus	--4	ASTM D638	2400	Mpa
	Tensile modulus	Tensile modulus	--3	ASTM D638	2360	Mpa
Bending modulus	50.0 mm Span7	ASTM D790	2450	Mpa
Bending modulus	Bending modulus	--8	ISO 178	2380	Mpa
bending strength	--8,9	ISO 178	64.0	Mpa
bending strength	bending strength	Yield, 50.0 mm Span7	ASTM D790	74.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			85 to 90	°C
drying time			4.0	hr
Suggested maximum moisture content			0.040	%
Suggested injection volume			40 to 80	%
Temperature at the rear of the barrel			215 to 250	°C
Temperature in the middle of the barrel			220 to 255	°C
Temperature at the front of the material cylinder			230 to 260	°C
Spray nozzle temperature			220 to 255	°C
Processing (melt) temperature			240 to 270	°C
Mold temperature			60 to 85	°C
Back pressure			0.300 to 1.00	Mpa
Screw speed			30 to 80	rpm
Exhaust hole depth			0.038 to 0.076	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	97.0	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span11	ISO 75-2/Bf	98.0	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	84.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span11	ISO 75-2/Af	84.0	°C
Vicat softening temperature	--		98.0	°C
	Vicat softening temperature	--	ISO 306/B50	95.0	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	99.0	°C
Ball Pressure Test	83 to 87°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	8.4E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	8.3E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	9.4E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	9.4E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Outdoor applicability		UL 746C	f1
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.20	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.50	%
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.75	%
	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.40 - 0.70	%
	Shrinkage rate	Shrinkage rate	Flow 2	Internal Method	0.40 - 0.70	%
Melt Volume Flow Rate (MVR)	260°C/5.0 kg	ISO 1133	9.00	cm3/10min
melt mass-flow rate	280°C/3.8 kg	ASTM D1238	7.2	g/10 min
	melt mass-flow rate	260°C/5.0 kg	ASTM D1238	7.1	g/10 min
	melt mass-flow rate	melt mass-flow rate	220°C/10.0 kg	ASTM D1238	8.8	g/10 min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	100

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

ASA XTWM206-BK1C091 SABIC INNOVATIVE US

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index