Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.57 g/cm³ |
| Apparent density | | ISO 60 | 0.70 g/cm³ |
| Shrinkage rate | | ISO 2577 | 0.50 % |
| Shrinkage rate | | ISO 2577 | 0.30 % |
| Water absorption rate | | ISO 62 | 30.0 mg |
| Shrinkage rate | | ISO 2577 | 0.25 % |
| Shrinkage rate | | ISO 2577 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 350 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Compression molding pressure | | | >15.0 MPa |
| Compression molding temperature | | | 160to190 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 10500 MPa |
| tensile strength | | ISO 527-2/5 | 65.0 MPa |
| Flexural modulus | | ISO 178 | 10500 MPa |
| bending strength | | ISO 178 | 125 MPa |
| compression stress | | ISO 604 | 250 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 2.2 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| relative permittivity | | IEC 60250 | 10.0 |
| Dissipation Factor | | IEC 60250 | 0.25 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Surface Resistivity | | IEC 60093 | 1E+11 ohms |
| Volume resistivity | | IEC 60093 | 1E+12 ohms·cm |
| dielectric strength | | IEC 60243-1 | 26 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/C | 150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.