PVC

PVC Keysor PVC KC1260 Keysor-Century Corporation

Usages:
Containers food containers packaging blown containers cosmetic packaging food packaging
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	3.18mm	ASTM D256	800 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	3.18mm	ASTM D256	800 J/m

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2380 MPa
elongation	Break	ASTM D638	110 %
tensile strength	Break	ASTM D638	30.3 MPa
tensile strength	tensile strength	Yield	ASTM D638	40.0 MPa
Tensile modulus		ASTM D638	2380 MPa
bending strength	Yield	ASTM D790	82.7 MPa
Bending modulus		ASTM D790	3100 MPa
bending strength	Yield	ASTM D790	82.7 MPa
Bending modulus		ASTM D790	3100 MPa
elongation	Break	ASTM D638	110 %
tensile strength	Break	ASTM D638	30.3 MPa
tensile strength	tensile strength	Yield	ASTM D638	40.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	62.2 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	62.2 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	190°C/21.6kg	ASTM D1238	7.5 g/10min
density		ASTM D792	1.29 g/cm³
melt mass-flow rate	190°C/21.6kg	ASTM D1238	7.5 g/10min
density		ASTM D792	1.29 g/cm³

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreD	ASTM D2240	78
Shore hardness	Shore hardness	ShoreD	ASTM D2240	78

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.